PVC Emulsion, Paste Resin & Latex Manufacturer
KaneVinyl PVC™
Kaneka Paste Polymers manufacture KaneVinyl PVC using two sophisticated manufacturing techniques — Micro-suspension Grade and Emulsion Grade. We offer the highest quality PVC Emulsion, PVC Paste Resin Manufacturer and PVC latex which meets a wide range of market demands, such as artificial leather, wall coverings, floor coverings and many more. Kaneka’s persistent pursuance of innovation and investment in R&D to meet market and customer demands.
Product Name
PVC M.Suspension (Paste)
Application
- Leather (PSM-31)
- Disposable Glove (PSH-31)
- Non Disposable Glove (PSM-30)
- Cap Seal (PSH-10)
- Tarpaulin (PSH-36)
- Wallpaper (PSL-75)
- Flooring (XH-27C)
PVC Emulsion (Paste)
- PU Sealant (EH-251)
- Non Penetration (EM-552)
- Yoga Mat (EL-31)
- Can Coating (EH-150)
- High Thixotropic (EM-235)
Key Highlights
Non-Penetration
Controlling the thickness and weight of the PVC layer on the substrate requires the non-penetration feature. KaneVinyl non-penetration grades are specially designed with different particle sizes to prevent excessive penetration of the PVC layer into the substrate. It also features dilatant behaviour for better PVC weight control during the dipping process.
Application: Working Glove
Recommended grade: EM-552
Rheology Modifier
Plastisol flow behaviour has a significant impact on PVC product manufacturing; hence a rheology modifier is frequently used in plastisol preparation. KaneVinyl grades are designed to handle all types of fluid flow requirement, including Newtonian, pseudoplastic, and dilatant.
Recommended grade: Pseudoplastic modifier: EM-235, EM-271
Dilatant modifier: EM-550 series
Matt Surface
Certain applications necessitate a matt appearance on the PVC end product. KaneVinyl cross-linked grade features a matt surface finishing feature. With special cross-linked technology, the light reflection on the PVC surface layer will be scattered around, resulting in a low glossy surface effect.
Application: Flooring, Screen-printing
Recommended grade: XH-27C
FDA compliance
Compliance with the Food and Drug Administration (FDA) is required for PVC products used in food, medicines, cosmetics, and some medical equipment. FDA compliance grades from KaneVinyl are tested by an authorised laboratory.
Recommended grade: PSM-30, PSH-10
Sustainability Commitment : Our Future
KPP focus on conservation of biodiversity , building on foundation of environmental sustainability such as water conservation & energy saving. In year 2021, KPP launched PVC Latex with *30% reduction of energy and *90% reduction in steam consumption. Read more details in brochure to know about KaneVinyl Latex
In year 2022, KPP has partnering Sanvic Inc to promote “Biomass Composite Materials” which target to recycle grain(s) and tea leaves which are highly sustainable materials replacing fossil fuels derivatives resource for consumer products. Read more on the details in article downloadable at right.
Sustainability has no boundaries . KPP also partnering Kaneka Asia to develop turbine blade alternatives using PVC. With major developing countries working on decarbonization & Zero carbon emission by 2050, demand for sustainable energy like wind turbine will be important . Current material (Balsa Wood) is South America’s unique wood, with limited supply & potential deforestation in near future, we are here for the future as alternatives. Read more on the details in article downloadable at right.
Grade
Micro-suspension Grade
| Grade Name | K Value | Viscosity (mPas) | Recommended Applications | Features | SDS |
|---|---|---|---|---|---|
| PSH-25 | 80 | 3,000 | Automotive artificial leather, Floor covering | Excellent physical properties, Low fogging | Download |
| PSH-31 | 77 | 2,000 | Artificial leather, Disposable glove, Flooring covering | Good physical properties, General use | Download |
| PSH-36 | 76 | 2,500 | Tarpaulin, Artificial leather | Good physical properties, Good air release | Download |
| PSH-10 | 75 | 3,500 | Toys, Cap seal, Underbody coating | High transparency, Low water absorption, Good electric resistance | Download |
| XH-27C | 74 | 3,000 | Floor covering | Matt finishing, Good air release | Download |
| PSM-30 | 73 | 6,000 | Glove, Underbody coating | Thixotropic rheology | Download |
| PSM-31 | 73 | 2,500 | Artificial leather, Toys, Tarpaulin | General use | Download |
| PSM-71 | 73 | 2,500 | Toys, Foam layer | Fast gelation, Gloss surface | Download |
| PSM-72E | 73 | 2,000 | Glove, Toys | Good air release | Download |
| PSL-31 | 66 | 2,000 | Artificial leather (Foam) | Fast gelation, Good foam-ability | Download |
| PSL-75 | 66 | 4,500 | Floor covering, Wallpaper | High blowing ratio, Low water absorption | Download |
| SL-273 | 60 | 5,000 | Wallpaper (High speed coating) | High blowing ratio, Thixotropic rheology | Download |
Emulsion Grade
| Grade Name | K Value | Viscosity (mPas) | Recommended Applications | Features | SDS |
|---|---|---|---|---|---|
| EH-50 | 82 | 2,500 | Automotive artificial leather | Low VOC, Excellent phyiscal properties, High transparency | Download |
| EH-60 | 80 | 3,000 | Automotive artificial leather, Floor covering | Low VOC, Low Fogging, Excellent phyiscal properties | Download |
| EH-150 | 77 | 4,000 | Can Coating, Marking Film | Good physical properties | Download |
| EH-250 | 73 | 9,000 | Sealant | Low water absorption, Thixotropic rheology, High clarity | Download |
| EH-251 | 76 | 5,500 | Sealant | Low water absorption, Thixotropic rheology, High clarity | Download |
| EM-31 | 72 | 1,500 | Artificial leather, Coir Mat | Good physical properties | Download |
| EM-235 | 70 | 48,000 | High foam mat, Rheology modifier | High blowing ratio, Thixotropic rheology | Download |
| EM-271 | 70 | 63,000 | Underbody coating, Rheology modifier | Thixotropic rheology | Download |
| EM-550 | 73 | 4,500 | Working glove | Good physical properties, Dilatant rheology | Download |
| EM-551 | 73 | 2,500 | Working glove | Good physical properties, Dilatant rheology | Download |
| EM-552 | 79 | 2000 | Working glove | Excellent physical properties, Excellent dilatant rheology | Download |
| EL-31 | 68 | 2,500 | Carpet backing, Foam mat | Fast blowing speed, Good foam-ability | Download |
| EL-33 | 66 | 3,500 | Carpet backing, Foam mat | Fast blowing speed, Good foam-ability | Download |
| EL-231 | 68 | 6,000 | Foam mat, High foam material | High blowing ratio, Thixotropic rheology | Download |
* Viscosity data for EM-55X grades are calculated based on Resin/DOTP:100/120. Other Emulsion grades are 100/80
* Viscosity data for Microsuspension grade are calculated based on Resin/DOTP : 100/60
Our Value Services
With our fully equipped polymer laboratory, Kaneka provides leading expertise in :
Application Development
Formulation Development
Compound Mixing (Lab Scale)
PVC Properties Testing
Technical Service
Market Insight